POM美国杜邦588P 高刚性高耐磨

DuPont Performance Polymers Delrin® 588P NC010 Acetal Homopolymer (Unverified Data**) 物性表
物理性能	额定值 (公制)	额定值 (英制)	测试方法
密度	1.42 g/cc	0.0513 lb/in³	ISO 1183
吸水率	0.30 %
@Temperature 23.0 °C
0.30 %
@Temperature 73.4 °F
Equilibrium 50%RH; ISO 62, Similar to
线性成型收缩率,Flow	0.019 cm/cm
@Thickness 2.00 mm
0.019 in/in
@Thickness 0.0787 in
ISO 294-4
线性成型收缩率，横向	0.018 cm/cm
@Thickness 2.00 mm
0.018 in/in
@Thickness 0.0787 in
ISO 294-4
熔体流动速率	15 g/10 min
@Load 2.16 kg, Temperature 190 °C
15 g/10 min
@Load 4.76 lb, Temperature 374 °F
ISO 1133
机械性能	额定值 (公制)	额定值 (英制)	测试方法
洛氏硬度（R 级）	120	120	ISO 2039/2
抗张强度(屈服)	73.0 MPa
@Temperature 23.0 °C
10600 psi
@Temperature 73.4 °F
ISO 527
伸长率 (断裂)	25 %
@Temperature 23.0 °C
25 %
@Temperature 73.4 °F
nominal; ISO 527
屈服伸长率	12 %
@Temperature 23.0 °C
12 %
@Temperature 73.4 °F
ISO 527
拉伸模量	3.20 GPa
@Temperature 23.0 °C
464 ksi
@Temperature 73.4 °F
ISO 527
简支梁缺口冲击强度	0.800 J/cm²
@Temperature 23.0 °C
3.81 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
电气性能	额定值 (公制)	额定值 (英制)	测试方法
相比耐漏电起痕指数(CTI)	600 V
@Thickness 3.00 mm, Temperature 23.0 °C
600 V
@Thickness 0.118 in, Temperature 73.4 °F
UL 746A
热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	178 °C	352 °F	10°C/min; ISO 11357-1/-3
载荷下热变形温度(1.8 MPa)	97.0 °C	207 °F	ISO 75-1/-2
UL RTI	50.0 °C
@Thickness 0.800 mm
122 °F
@Thickness 0.0315 in
UL 746B
110 °C
@Thickness 1.50 mm
230 °F
@Thickness 0.0591 in
UL 746B
110 °C
@Thickness 3.00 mm
230 °F
@Thickness 0.118 in
UL 746B
UL RTI，机械冲击	50.0 °C
@Thickness 0.800 mm
122 °F
@Thickness 0.0315 in
UL 746B
85.0 °C
@Thickness 1.50 mm
185 °F
@Thickness 0.0591 in
UL 746B
90.0 °C
@Thickness 3.00 mm
194 °F
@Thickness 0.118 in
UL 746B
UL RTI，机械无冲击	50.0 °C
@Thickness 0.800 mm
122 °F
@Thickness 0.0315 in
UL 746B
90.0 °C
@Thickness 1.50 mm
194 °F
@Thickness 0.0591 in
UL 746B
95.0 °C
@Thickness 3.00 mm
203 °F
@Thickness 0.118 in
UL 746B
可燃性(UL94)	HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
IEC 60695-11-10
HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
IEC 60695-11-10
HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
IEC 60695-11-10
HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
UL94
HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
UL94
HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
UL94
加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	215 °C	419 °F	Optimum; Injection Molding
210 - 220 °C	410 - 428 °F	Injection Molding
模具温度	90.0 °C	194 °F	optimum; Injection Molding
80.0 - 100 °C	176 - 212 °F	Injection Molding
干燥温度	80.0 °C	176 °F	Injection Molding
干燥时间	2.00 - 4.00 hour	2.00 - 4.00 hour	Injection Molding
水分含量	<= 0.20 %	<= 0.20 %	Injection Molding
材料描述		测试方法
外观	Natural Color	
Extrudable - Cast Film	Yes	
Extrudable - Sheet	Yes	
Extrudable - Tubing	Yes	
Extrudable - Wire and Cable	Yes	
特性	Creep Resistance, Good	
Dimensional Stability, Good	
Fatigue Resistant	
Homopolymer	
Stiffness, High	
Strength, High	
Viscosity, Medium	
形式	Pellets	
Generic	Acetal (POM) Homopolymer	
Material Status	Current	
部件标识代码	>POM<	ISO 11469
Polymer Family	POM	
Polymer Type	POM Homopolymer	
加工方法	Injection Molding	
产品分类	Unreinforced Resins	
树脂识别	POM	ISO 1043
符合RoHS指令	Contact Manufacturer	
Ultrasonic Weldable	Yes	
用途	Fasteners	
Gears	
General Purpose	
Parts, Engineering